摘要 :
The incorporation of different types of buffer layers has demonstrated to improve the efficiency of Cu_2ZnSnS_4 (CZTS) thin film solar cells. The materials tested as buffer layers were Cadmium Sulphide (CdS), Zinc Sulphide (ZnS) a...
展开
The incorporation of different types of buffer layers has demonstrated to improve the efficiency of Cu_2ZnSnS_4 (CZTS) thin film solar cells. The materials tested as buffer layers were Cadmium Sulphide (CdS), Zinc Sulphide (ZnS) and Cadmium Zinc Sulphide (Cd_(7.23)Zn_(2.77)S_(10)). The effect of the buffer layer and the absorber layers on the structural, morphological and optical properties of the films was studied. As grown CZTS thin films made with SILAR method were annealed at 550 °C in the sulfur atmosphere for 60 min to improve the crystallinity of the material. X-ray diffraction (XRD) and Raman studies confirm the formation of kesterite structure in CZTS thin film. CdS, ZnS and Cd_(7.23)Zn_(2.77)S_(10) thin films also confirm crystalline nature with crystallite sizes being 9 nm, 13 nm and 14 nm respectively. Leaf, flower and petal−like morphologies of CdS, ZnS and Cd_(7.23)Zn_(2.77)S_(10) thin films respectively have been confirmed by Field Emission Scanning Electron Microscopy (FESEM). The electrical properties of the completed CZTS solar cells were also examined. From the obtained J-V characteristic curves upon illumination of the heterojunction solar cells, we calculated the power conversion efficiency to be 0.76%, 1.00% and 1.24% for the FTO/ZnO/ZnS/CZTS/Ag, FTO/ZnO/CdS/CZTS/Ag and FTO/ZnO/Cd_(7.23)Zn_(2.77)S_(10)/CZTS/Ag respectively.
收起